3, 4-epoxy-cyclohexane-1-carboxaldehyde acetals



Patented Oct. 12, 1965 3,211,750 R1 R1 R2 3,4-EPOXY-CYCLOHEXANE-l-CARBOX- O ALDEHYDE ACETALS F I \g Hans Batzer, Rainweg 7, Arlesheim, Switzerland; Willy fi -t Fisch, Stelzenaclrerstrasse 11, Binningen, Switzerland; 5 0 I I Q 0 O I Q and Erwin Nikles, Untere Rebgasse 16, Basel, Switzerland No Drawing. Filed Sept. 3, 1963, Ser. No. 306,318 0 R7 0 R4 Claims priority, application Switzerland, Sept. 17, 1959,

78,334/59; Mar. 25, 1960, 3,374/60 8Claims. (or. 260-3401) 10 (III) This application is a continuation-in-part of application compounds of the formula Serial No. 54,582, filed September 8, 1960 and now abandoned. R3 0 R9 0 The present invention provides new acetals that con- 0 C A tam at least two epoxide groups and correspond to the formula I 0 R2 R1 R \C/ R4 0 R7 3 R9 0 i Y R5 R6 I (IV) I I and compounds of the formula 8 O \C Rg\ /R1 R;\ 0 /R9 o o o-ofi z-o-A: Ra Re 11 (I) O 0 R in which R to R each represents a hydrogen atom or a \I I/ a monovalent substituent such as a halogen atom, an alkoxy group or an aliphatic, cycloaliphatic, araliphatic, or aro- R4 0 R1 matic hydrocarbon radical, and R and R together may (v) also represent an alkylene radical such as a methylene group; Z represents a trivalent aliphatic, cycloaliphatic or araliphatic hydrocarbon radical with at least 3 carbon atoms, none of which has more than a single free valence, and no carbon atom having such a free valence carries a hydroxyl group; G represents a group in which R and R taken together form a member selected from the class consisting of two hydrogen atoms, two lower alkyl radicals having 1 to 4 carbon atoms, and one methylene radical, R R R R R R and R each represents a member selected from the class consisting of hydrogen atom and lower alkyl group having 1 to 4 carbon atoms, Z represents the hydrocarbon radical of a trihydric aliphatic alcohol, Y represents the hydrocarbon /0, /C=0 or /0= radical of a dicarboxylic acid, A is a member selected 0 from the class consisting of epoxyalkyl and epoxycycloalkyl, A is a member selected from the class consisting of n is a small whole number and Y represents an aliphatic, epoxyalkyl, epoxycycloalkyl and the radical of the cycloaliphatic, araliphatic or aromatic radical with n free mula valences and, when 11:1, the radical Y must contain at 0-011, 011,

least one epoxide group. More particularly, the present invention provides new F diepoxide compounds of the formulae R FOE? I R-OH OH R, /R6 R1\ /R2 (VI) R3 0 En 0 0 R9 0 R3 where R is selected from the class conslstmg of hydrogen 5 atom and the methyl group, and n represents an integer of 0 I I Rs 0 0 R9 I O at least 1 and at the most 2.

The acetals containing epoxide groups of the present process are obtained by treating an unsaturated acetal of R7 the general formula Rs Ru Ru Rs (1) 7 R2 R1 compounds of the formula R9 0 Ra\ /R1 n, o o oh zo- Y \O/ o o-c z-0ooz 011-0 0 o I I R, o t) o R, I 0

\ Ra RB 11 (H) o O 0 0 m WhlCh R to R Z, G and n have the same meanings as 4 7 7 4 in the Formula I and Y represents an aliphatic, cyclo- R5 Ra Ra Ra (H) aliphatic, araliphatic, or aromatic radical and, when n=1,

the radical Y contains at least one epoxidizable group compounds of the formula or an epoXide groupwith an epoxidizing agent.

The term epoxidizable group refers above all to residues containing epoxidizable carbon-to-carbon double bonds, such as an allyl, butenyl or tetrahydrobenzyl radical; by treating such carbon-to-carbon double bonds, for example with organic peracids, they can be epoxidized t form the 1:2-epoxide group.

The term epoxidizable group further designates radicals containing a halohydrin grouping in which Hal represents a halogen atom, such as a 3- methylglycerol-u-monochlorohydrin radical or a glycerolot-mono-chlorohydrin radical. It is known that such a halohydrin group can likewise be converted into a 1:2- epoxide group by treatment with a dehydrohalogenating agent.

The starting materials of the Formula II are obtained, for example, when in a first stage an aldehyde of the formula in which A represents a hydrogen atom or a lower alkyl radical.

The aldehydes of the Formula III are derivatives of tetrahydrobenzene; as examples may be mentioned A tetrahydrobenzaldehyde, 6-methyl-A -tetrahydrobenzaldehyde and 2:5-endomethylene-A -tetrahydrobenzaldehyde.

Suitable polyalcohols of the Formula IV are: Triols such as glycerol, trimethylolethane, trimethylolpropane, butanetriol-( 1 :2:4), 1:2 6-hexanetriol, 2:4-dihydroxy-3- hydroxymethylpentane; halohydrins such as glycerol-otmono-chlorohydrin, glycerol-B-chlorohydrin, glycerol-ubromohydrin and glyceric acid.

The acetylation may follow the known pattern, and consist for example in heating an aldehyde of the Formula III together with a dialcohol or polyalcohol IV in the presence of an acid catalyst such, for example, as hydrochloric acid or para-toluenesulfonic acid.

Furthermore 1 mole of an aldehyde of the formula III may be added on to 1 mole of an epoxide of the formula In either case the reaction product is an acetal of the The conversion of the compound (VI) into the unsaturated acetal of the Formula II depends on the nature of the functional group G. A suitable method is condensation, such as etherification, esterification or reesterification with a reactive compound containing, for example, one or more mobile halogen atoms, or groups containing active hydrogen atoms. Likewise suitable is an additive combination of an cup-unsaturated compound with one or several carbon-to-carbon double bonds.

In this connection two basically different cases must be distinguished:

(l) The reactive compound used for the reaction with the acetal (VI) contains an epoxide group or an epoxidizable group, for example an epoxidizable carbon-tocarbon double bond which does not participate in the reaction with the acetal (VI). In this case it is possible to use reactive compounds containing only one reactive gruop such, for example, as a mobile halogen atom, a hydroxyl or carboxyl group.

(2) The reactive compound used is free from epoxide groups or epoxidizable groups that do not undergo reaction already with the acetal (VI). In this case the reactive compounds must contain at least two reactive groups, such, for example, as mobile halogen atoms, hydroxyl or carboxyl groups or olefinic carbon-to-carbon double bonds capable of addition on to hydroxyl groups or the like.

In case (1) there may be mentioned as compounds that contain epoxide groups or are epoxidizable and contain a reactive group as defined above: epihalohydrins such as epichlorohydrin; dihalohydrins such as glycerol dichlorohydrins; unsaturated alcohols such as allyl alcohol, A tetrahydrobenzyl alcohol and 6-methyl-A -tetrahydrobenzyl alcohol; glycerol diesters of unsaturated fatty acids such as glycerol dioleate or glycerol dilinoleate; unsaturated carboxylic acids and functional derivatives thereof such as A -tetrahydrobenzoic acid, 6-methyl-A -tetrahydrobenzoic acid, oleic acid, elaidic acid, ricinoleic acid, linoleic acid, ricinenic acid, tall oil acids, soybean fatty acids, linseed oil acids, tung oil acids, crotonic acid, acrylic acid, methacrylic acid, acrylic acid methyl ester, acrylyl chloride and the like; unsaturated halides, such as allyl bromide and allyl chloride; unsaturated acetals, such as 3-vinyl-2z4-dioxospiro(5:5)undecene-8 and 3-propenyl- 7-methyl-2 4-dioxospiro 5 5 undecene-8.

In case (2) there may be mentioned as saturated or unsaturated compounds containing at least two reactive groups as defined above: Saturated polyalcohols such as ethylene glycol, diethylene glycol, triethylene glycol, butanediol-124, glycerol, sorbitol, penta-erythritol; unsaturated poly-alcohols such as butene-(2)-diol-1:4, l:l-bis- [hydroxymethyl]-cyclohexene-3 and 1 l-bis-[hydroxymethyl]-6-methylcyclohexene-3; glycerol monoesters of unsaturated fatty acids such as glycerol monooleate or glycerol monolinoleate; diphenols and polyphenols such as resorcinol, hydroquinone, bis-[para-hydroxyphenyl]- methane and 2:Z-bis-[para-hydroxyphenyl]-propane; carbonic acid, phosgene and polycarboxylic acids, such as oxalic, succinic, adipic, sebacic, hexahydrophthalic, phthalic, terephthalic, maleic, fumaric, tetrahydrophthalic, pyromellitic acid and functional derivatives thereof such as their acid halides and acid anhydrides; furthermore polyhalogen compounds such as dichloromethane, dichloroethane, dibromoethane, dichlorobutene and the like; also compounds containing two or more carbon-to-carbon double bonds capable of adding on to hydroxyl groups with formation of an ether bridge, such as ethylene glycolbis-acrylic acid esters, NzN-bis-[acrylamido1-methane and NzN':N"-triacrylyl-hexahydrotriaz-ine-1 :3 :5; and bisacetals of acrolein, such as 3:9-divinylspiro-bi-(meta-dioxane).

Furthermore, unsaturated acetals of the Formula II can be prepared directly by acetalizing 2 moles of an 5 6 aldehyde of the Formula III with 1 mole of a polyalcohol CH2 6 CH2 of the formula CE CHOfi C]E[ ]O-t J-C I \CH O/ \O- --OH: I \O HO OH on CH-R R'OH on ofi ofi (x no on (v11 in which R and R each represents a hydrogen atom or a lower alkyl radical with 1 to 4 carbon atoms.

As examples of polyalcohols (VII) there may be men- Such epoxides are bright resins which are at room tioned diglycerol and ethylene glycol-diglyceric ether. temperature liquid or fusible and can be converted with Finally, unsaturated acetals of the Formula II may also suitable curing agents such, for example as dicarboxylic be prepared directly by acetalizing 1 mole of an aldehyde acid anhydrides, into clear and bright, cured products of the Formula III with 1 mole of a dialcohol of the having excellent technical properties.

formula 15 The epoxidized acetals of the invention react with the conventional curers for epoxide compounds; they can therefore be cross-linked or respectively cured in the presence of such curing agents in the same manner as other polyfunctional epoxide compounds or epoxy resins re- HO (VH1) spectively. As such curing agents there may be mentioned basic or more especially acidic compounds.

The following have proved suitable: Amines and in which the radical Y' contains an epoxidizable group. id h as li h ti d ti primary, SecomL EXaIhptes ot dialoohols are! Addhets 0t tfiols, ary and tertiary amines, for example mono-, diand trisuch as glycerol with dicyclopentadiene; Diels-Alder adbutylamines, para-phenylenediamine, bis-[para-a i du ts of monoahyl ethefs of tfiols, Such as glycerolphenyl]-methane, ethylene-diamine, N1N-diethylethylenemonoahyl ether, With oyclopehtadiehediamine, diethylenetriamine, tetra-[hydroxyethyH-diethyl- I11 the p of the Present invention the aeetals of enetriamine, triethylenetetramine tetraethylenepentamine, the F r 11 a treated With ePoXidiZihg agents- The N:N-dimethylpropylenediamine, trimethylamine, diethylepoxidation of the carbon-to-carbon double bonds leadamine, i h l i i h bases, piperidine,

ing to the compounds of the present inv n i n is P perazine, guanidine and guanidine derivatives such as formed y a conventional method, Preferably h the phenyl diguanidine, diphenylguanidine, dicyandiamide, aid of organic P Such as Peraoetto, PefhehZoio, formaldehyde resins with aniline, urea and melamine; Pefadipio, 'p p acid the like- A further polymers of aminostyrenes, polyamides, for example those Suitable ePoXidiZihg agent is hypoohlofohs acid, in a first prepared from aliphatic polyamines and dimerized or tri- Stage H001 being added to he do l bond and ill a merized unsaturated fatty acids, isocyanates, isothiocya- Second Stage the epoxide group being formed under the nates; polyhydric phenols, for example resorcinol, hydroaction of an agent capable of splitting oif hydrogen chloi bi [4 h d h l -di h l th i ride, for example a strong alkali. none, phenol-aldehyde resins, oil-modified phenol-alde- 111 Correspondence With What has been Said above 40 hyde resins; reaction products of aluminum alcoholates oerhhlg the Significance of the term epoXidileble g p and phenolates with compounds of tautomeric reaction of the treatment according to the invention with epoxidizing th t of th t ti esters, F i d Lcraft cataagents hlohldes also reaction With an agent Capable 0f lysts such as aluminum chloride, antimony chloride, tin Splitting oft hydrogen de, such as p ta hydroXide tetrachloride, zinc chloride, boron trifluoride and comor sodium hydroxide, upon halohydrin groups, for eXamplexes thereof with organic compounds; metal fluorobople t g y mohoohlorohydrih p, to form the rates and phosphoric acid. Preferred curing agents are corresponding liz'epoxide P a y yl g ppolybasic carboxyl acids and hydrides thereof, for

When the acetal of the Formula II contains in addition example hth li anhydride methylendomethylene tet. to epoxidizable carbon-to-carbon double bonds halohyrahydrophthalic anhydride, dodecenyl-succinic anhydride,

drin groups, the epoxidation takes place in two stag s: hexahydrophthalic anhydride, hexachloro-endomethylene- The epoxidation may yield, in addition to the diepoxldes t t hydrophthalic anhydride or endomethylene-tetrahyor polyepoxides respectively, by way f sid reactions also drophthalic anhydride, or mixtures thereof; maleic or ep xi s that are Wholly y Partially y y that succinic anhydride. If desired, an accelerator, such as is to say compounds in which the epoxide group of the a tertiary amine or a strong Lewis base, for example an poly-epoxide of the Formula I has been wholly or pam alkali metal alcoholate, and advantageously also a polytially hydrolyzed to hydroxyl groups. hydroxy compound, such as hexanetriol or glycerol, may

It has been observed that the presence of such byhe further added. products generally has a favorable influence on the tech It h been ob erved th t hen n epoxy e i f the nical properties of the Cured polyepoxides- It is t r invention is cured with a carboxylic anhydride it is of fore, in general, advantageous not to isolate e P 0 advantage to use for every gram equivalent of epoxide polyepoxides from the reaction mixture. groups only about 0.3 to 0.9 gram equivalent of anhy- Particularly advantageous technical properties are dride groups. When a basic accelerator is used, such as found, for example, in the diepoxides of the formula an alkali metal alcoholate or an alkali metal salt of a CH; O CH; CY1 CO CHr- -O CH; 06: \CIE['CH CH O i: i ]m1 (H) CH- \CHC. \CH O 0 OH9 n-I. CHF 0 \O \CH OH-R R'GH C (IX) In which R and R each represents a hydrogen atom or a carboxylic acid, up to 1.0 gram equivalent of anhydride lower alkyl radical with 1 to 4 carbon atoms, Y an aligroups may be used. phatic, cycloaliphatic, araliphatic or aromatic hydrocar- The term curing as used in this context signifies the hon radical, and m and it each 1 or 2; also in the diconversion of the aforementioned epoxide compounds epoxides of the formula 7 into insoluble and infusible resins.

Accordingly, the present invention also includes curable mixtures containing an epoxidized acetal of the invention as well as a curing agent for epoxy resins, preferably a dior polycarboxylic acid anhydride.

Advantageously, the curable mixtures of the invention further contain a share of otherwise suitable acetals whose epoxide groups however have been wholly or partially hydrolyzed to hydroxyl groups, and/or also other cross-linking poly-hydroxy compounds, such as hexanetriol. It is, of course, possible to add to the curable epoxide compounds also other epoxides such, for example, as monoglycidyl or polygly-cidyl ethers of monoalcohols or polyalcohols such as butanol, 1:4- butanediol of glycerol, or of monophenols or polyphenols such as resorcinol, bis-[4-hydroxyphenyl]-dimethylmethane or condensation products of aldehydes with phenols (novolaks); also polyglycidyl esters of polyca-rboxylic acids such as phthalic acid; also aminopolyepoxides such as are obtained for example by dehydrohalogenating a reaction product of an epihalohydrin with a primary or secondary amine, such as n-butylamine, aniline or 4:4-di-(monomethylamino)-diphenylmethane.

Furthermore, the curable epoxide compounds or mixtures thereof with curing agents can be admixed at any stage prior to the curing with fillers, plasticisers, coloring matters and the like. Suitable extenders and fillers are, for example, asphalt, bitumen, glass fibers, mica, quartz meal, cellulose, kaolin, finely dispersed silicic acid (Aerosil) or metal powders.

The mixtures of the epoxide compounds of the invention with the curing agent can be used without or with fillers, if desired in the form of solutions or emulsions, as textile assistants, laminating resins, paints, lacquers, dipping resins, casting resins, coating compositions, pore fillers and putties, adhesives, moulding compositions or the like, as well as for the manufacture of such products. The new resins are especially valuable for use as insulating compounds for the electrical industry.

In the following, parts and percentages are by Weight, the relationship between part by weight and part by volume being the same as that between the kilogram and the liter:

PREPARATION OF THE INTERMEDIATES A -Tetrahydrobenzal glycerol A solution of 184 parts of glycerol, 220 parts of A tetrahydrobenzaldehyde and 4 parts of para-toluenesulfonic acid in 500 parts by volume of benzene is heated in a cyclic distillation apparatus (described by Batzer and co-workers in Makromolekulare Chemie 7 (1951) page 82) until (after about 20 hours) 25 parts by volume of water have separated; the remainder of the water of reaction is absorbed by the drying agent. The cooled solution is agitated with 100 parts by volume of water and then with 50 parts by volume of sodium carbonate solution, dried over sodium sulfate and the benzene is evaporated. The residue is subjected to fractional distillation, to yield 290 parts of a main fraction (=75% of the theoretical), boiling at 98100 C. under a pressure of 0.4 mm. Hg.

To identify this product it is subjected to catalytic hydrogenation and the hydroxyl number is determined, being 263; double bonds =5.7 equivalents (theoretical values for the compound of the empirical formula C H O OH number :308, double bonds :55).

In exactly the same manner as described above equivalent amounts of the following aldehydes and triols can be condensed to yield cyclic acetals:

6-methyl-M-telrahydrobenzal glycerol Found:

Acetal from A -telrahydrobenzaldehyde and 1:2:6-hexanetri0l Acetal: B.P. 126-128 C. under 0.08 mm. Hg pressure. C H O calculated: C, 68.99%; H, 9.80%. Found: C, 69.15%; H, 10.03.

2:5-endomethylene-M-tetralzydrobenzal glycerol 244 parts of 2:5-endomethylene-A -tetrahydrobenzaldehyde and 184 parts of glycerol are condensed in a cyclic distillation apparatus in the presence of 500 parts by volume of benzene, 1 part of anhydrous zinc chloride and 1 part by volume of concentrated phosphoric acid, with 33 parts of water separating out. The solution is filtered and evaporated and the residue is distilled in a high vacuum, to yield 310 parts of the cyclic acetal boiling at 97100 C. under 0.04 mm. Hg pressure.

C H O calculated: C, 67.32%; H, 8.22%. C, 67.18%; H, 8.26%.

When equivalent amounts of aldehyde and triol are condensed as described above, the following products are obtained:

Found:

Acetal from 6-methyl-A -tetrahydrobenzaldehyde and] :2 :4-butanetriol B.P. 103-105 C. under 0.2 mm. Hg pressure.

Acetal from 6-methyl-A -tetrahydrobenzaldehyde and 1 :1 :1 -trimethyl0lpropane B.P. 119120 C. under 0.2 mm. Hg pressure.

In the following examples of the performance of the present process commercial peracetic acid of about 42% strength has been used; it contains in addition to acetic acid about 3% of hydrogen peroxide, 10% of water and 1% of concentrated sulfuric acid. Unless otherwise indicated, the sulfuric acid is neutralized prior to use with about 2% of anhydrous sodium acetate.

EXAMPLE 1 198 parts of 6-methyl-A -tetrahydrobenzal glycerol are added dropwise at 2-10 C. to a solution of 49.5 parts of phosgene in 800 parts by volume of anhydrous benzene. The mixture is allowed to heat up to room temperature, the pyridine hydrochloride is filtered 0E and the filtrate is washed in the cold with 2 N-hydrochloric acid, 2 N-sodium hydroxide solution and a molar monosodium phosphate solution. The solution is dried over anhydrous sodium sulfate, filtered and evaporated, whereby the carbonate is obtained as a highly viscous liquid.

For analytical purposes a specimen of the product is distilled:

B.P. 216217 C. under 0.02 mm. Hg pressure. n =1.5009.

C H O- calculated: C, 65.38%; H, 8.11%. C, 65.12%; H, 8.07%.

158 parts of the unsaturated carbonate are dissolved in 675 parts of ethyl acetate and the solution is treated with 163 parts of peracetic acid. The mixture is first cooled and then heated to and maintained at 40 C. After 5 /2 hours the theoretical amount of peracetic acid has been consumed. The whole is diluted with 500 parts by volume of ethyl benzene, washed twice with parts of water on each occasion and evaporated in a water-jet vacuum after having been diluted Wtih 2000 parts by volume of ethyl benzene. The residue is an amorphous resin containing 3.60 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula Found:

CHFO

EXAMPLE 2 A mixture of 396 parts of 6-methyl-A -tctrahydrobenzal glycerol, 146 parts of oxalic acid diethyl ester, 2 parts of sodium methylate and 500 parts by volume of toluene is heated on an oil bath maintained at about 130- 150 C. The alcohol formed is distilled off as an azeotropic mixture with toluene through a Raschig column of 30 cm. height. When 90% of the theoretical amount of ethanol have passed over, the solution is filtered and evaporated to leave the oxalate as a highly viscous liquid.

For analytical purposes a specimen of the product is distilled:

B.P. 232-235 n =1.5043.

C H O calculated: C, 63.98%; H, 7.61%. C, 64.17%; H, 7.59%.

A solution of 360 parts of the oxalate in 1200 parts of ethyl acetate is reacted for 4% hours with 350 parts of peracetic acid. The mixture is cooled, diluted with 4600 parts by volume of ethyl benzene, washed twice with 200 parts of water on each occasion and evaporated in a waterjet vacuum. The residue is freed from the last remnants of solvent by being heated for 3 hours at 120 C. in a high vacuum. The product contains 2.89 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of C. under 0.04 mm. Hg pressure.

Found:

this example has the formula O-OH CH -O on on OOH o CHO 0 CH g g CH? CH O OCH1 EXAMPLE 3 A mixture of 297 parts of 6-methyl-A -tetrahydrobenzal glycerol, 110 parts of adipic acid, 1 part of paratoluene-sulfonic acid and 1000 parts by volume of toluene is boiled in a cyclic distillation apparatus. After 10 hours, 21 parts of water have separated.

The solution is then cooled to 30 C. and in the course of one hour 320 parts of peracetic acid are added in portions. After 2 hours at 30 C. the theoretical amount of peracetic acid has been consumed. The solution is washed with water and 2 N-sodium carbonate solution until it is free from acid, dried over anhydrous sodium containing 3.00 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of A mixture of 396 parts of 6-methyl-A -tetrahydro benzal glycerol, 100 parts of succinic anhydride, 1 part of para-toluene-sulfonic acid and 250 parts of ethyl benzene is boiled for 20 hours in a cyclic distillation apparatus, while 15 parts of water are separated.

The succinic acid ester is epoxidized with 450 parts of peracetic acid for 3 hours at 30 C. The solution is washed with water and 2 N-sodium carbonate solution until it is free from acid, dried over anhydrous sodium sulfate, filtered and evaporated, to yield a viscid resin containing 2.21 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula C-CHg 011 -0 04 y l as. O o-on o o CHO CH3 CH3 EXAMPLE 5 A mixture of 36.8 parts of A -tetrahydrobenzal glycerol, 400 parts of dry benzene and 20 parts of pyridine is treated at 3 C. dropwise with 23.9 parts of sebacic acid dichloride while being cooled with a mixture of ice and sodium chloride. The mixture is warmed up to room temperature, washed three times with parts of water on each occasion, dried over anhydrous sodium sulfate and evaporated, to yield 51.8 parts of sebacate of tetrahydrobenzal glycerol.

42.5 parts of the above product are dissolved in 300 parts of ethyl acetate and reacted for 6 hours at 40 C. with 45 parts of peracetic acid. The cooled solution is diluted with 600 parts by volume of ethyl benzene, washed twice with 100 parts of water on each occasion, treated with 900 parts by volume of ethyl benzene and evaporated. The last remnants of the solvent are removed in a high vacuum at C. Yield: 43 parts of a liquid diepoxide containing 3.00 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula EXAMPLE 6 A mixture of 92 parts of A -tetrahydrobenzal glycerol, 37 parts of phthalic anhydride, 1 part of para-toluenesulfonic acid and 180 parts by volume of benzene is heated in a cyclic distillation apparatus for 5 hours at the boil. The solution is diluted with 100 parts by volume of benzene and treated with 20 parts of sodium acetate. In the course of 30 minutes 106 parts of peracetic acid of 42% strength are added while cooling and the mixture is allowed to react for one hour at 30 C. while being stirred. The solution is washed twice with 200 parts of water and twice with 40 parts by volume of saturated sodium carbonate solution (until an alkaline reaction has been established) and again with 50 parts of water, dried over sodium sulfate and evaporated, to leave a viscous resin containing 3.5 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula A mixture of 594 parts of 6-methyl-A -tetrahydrobenzal glycerol, 420 parts of A -tetrahydrobenzoic acid methyl ester, and 21 parts of sodium methylate solution (prepared from 2 parts of sodium and 19 parts of methanol) is heated in an oil bath at -160 C., the methanol formed being distilled off through a 30 cm. high Raschig column. When the distillation ceases, 500 parts by volume of toluene are added, whereupon an azeotropic mixture of methanol and toluene passes over at 64 C. The Whole distillate contains the theoretical amount of methanol. The mixture is allowed to cool, filtered and distilled. The resulting A -tetrahydrobenzoic acid ester boils at 153-158 C. under 0.2 mm. Hg pressure.

A solution of 432 parts of the above ester in 1000 parts by volume of benzene is treated with 60 parts of anhydrous sodium acetate. While stirring and cooling, 600 parts of peracetic acid of 44.6% strength are added within 40 minutes at 30 C. The mixture is allowed to react for about 2 hours longer at 30 C., cooled and washed three times with 350 parts of ice water and twice with 300 parts by volume of 2 N-sodium carbonate solution. The aqueous phase is extracted with 600 parts by volume of benzene. The solution of the epoxide is dried over sodium sulfate, filtered and evaporated, to yield 429 parts of a thickly liquid, colorless product containing 5.02 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula EXAMPLE 8 A mixture of 49.5 parts of 6-methyl-A -tetrahydrobenzal glycerol, 500 parts by volume of dry benzene and 32 parts of pyridine is treated at C. with 50.7 parts of undecylenic acid chloride while being cooled with a mixture of ice and sodium chloride. After having heated up to room temperature, the mixture is filtered and the filtrate is washed with 200 parts by volume of 2 N-hydrochloric acid, 200 parts by volume of 2 N-sodium carbonate solution and 100 parts by volume of a molar monosodium phosphate solution and evaporated. Distillation of the residue under 0.02 mm. Hg pressure yields at 160162 C. the undecylenic acid ester of 6-methyl-A tetrahydrobenzal glycerol in the form of a thinly liquid, colorless oil.

C H O calculated: C, 72.49%; H, 9.96%. C, 72.53%; H, 10.00%.

A mixture of 60 parts of the undecylenic acid ester, 235 parts of ethyl acetate and 80 parts of peracetic acid is allowed to react for 14 hours at 40 C. and then for 7 hours at about 30 C., after which time the theoretical amount of peracetic acid has been consumed. The solution is diluted with 500 parts by volume of ethylbenzene, washed twice with 150 parts of water, treated with another 250 parts by volume of ethylbenzene and evaporated in a water-jet vacuum, to yield 60 parts of a thinly liquid diepoxide containing 3.86 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula Found:

O-OH: a l o o-on 0 CH: 1 n

EXAMPLE 9 A mixture of 36.8 parts of A -tetrahydrobenzal glycerol, 200 parts by volume of dry benzene and 25 parts of pyridine is treated at -3 C. portionwise with 60.2 parts of oleic acid chloride, then heated to room temperature and the solution of the ester formed is washed four times with 100 parts of water, dried over anhydrous sodium sulfate, filtered and evaporated. The residue consists of 89.3 parts of the oleic acid ester of tetrahydrobenzal glycerol.

75.4 parts of the ester so obtained are mixed with 300 parts of ethyl acetate and in the course of /2 hour treated portionwise with 110 parts of peracetic acid. The whole is reacted for 3 hours at 40 C. The solution is diluted with 400 parts by volume of ethylbenzene, washed twice with 100 parts of water, treated with another 800 parts by volume of ethylbenzene and evaporated. The residue is a liquid epoxide containing 3.92 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula EXAMPLE 10 A mixture of 921 parts of A -tetrahydrobenzal glycerol, 5 parts by volume of boron trifluoride of 48% strength in ether is heated to 55 C. and treated dropwise with 462 parts of epichlorohydrin, while maintaining the temperature at 55 C. by external cooling. The mixture is then allowed to cool to room temperature and neutralized with 1.8 parts of powdered sodium hydroxide. (An identical reaction product is obtained by condensing 1 molecular proportion of epichlorohydrin with 1 molecular proportion of glycerol and acetalizing the resulting glycerolmonochlorohydrin ether with A -tetrahydrobenzaldehyde.)

The whole reaction product is dissolved in 2500 parts of ethyl acetate and slowly treated with 1100 parts of peracetic acid. After 6 hours at 30 C. the theoretical amount of peracetic acid has been consumed. The solution is diluted with 2000 parts by volume of ethylbenzene, washed with 1500 parts of water, treated with 3000 parts by volume of ethylbenzene and evaporated in a water-jet vacuum, to yield a product which contains 2.64 epoxide equivalents per kg.

A mixture of 1200 parts of the above monoepoxide and 2000 parts by volume of dry benzene is treated with 165 parts of finely powdered sodium hydroxide while being cooled at 2025 C. After one hour the sodium chloride formed is filtered off. The filtrate is washed with 250 parts by volume of a molar monosodium phosphate solution, dried over sodium sulfate, filtered and evaporated, to yield a liquid diepoxide containing 5.56 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula o-on,

A mixture of 297 parts of 6-methyl-A -tetrahydrobenzal glycerol, 500 parts by volume of dry benzene and 1.5 parts by volume of boron trifluoride of 48% strength in ether is heated to C. 139 parts of epichlorohydrin are stirred in dropwise. By supplying slight cooling the temperature is prevented from rising above 81 C. On completion of the addition of epichlorohydrin the whole is allowed to cool to room temperature and in the course of 15 minutes 60 parts of powdered sodium hydroxide are stirred in, while maintaining the temperature at 25 C. by cooling. After another 23 minutes the mixture is filtered and the filtrate is evaporated, and the residue is treated with 0.2 part by volume of glacial acetic acid and rapidly distilled (B.P. 117-142 C. under about 0.3 mm. Hg pressure). Fractional distillation through a Vigreux column yields the glycidyl ether boiling at 13l137 C. under 0.04 mm. Hg pressure. The product contains 3.90 epoxide equivalents per kg. (=99% of the theoretical).

Analysis.C H O calculated: C, 66.11%; H, 8.72%; O, 25.17%. Found: C, 66.17%; H, 8.80%; O, 25.10%.

178 parts of the above glycidyl ether are diluted with 500 parts by volume of benzene and treated with 15 parts of anhydrous sodium acetate.

While cooling at about 30 C., parts of peracetic acid of 44.6% strength are added in portions within hour. The whole is allowed to react for 1 hour and 50 minutes longer at about 30 C. and then cooled. The benzene solution of the epoxide is washed three times with 200 parts by volume of ice water, 200 parts by volume of 2 N-sodium carbonate solution and parts by volume of monosodium phosphate solution, and the aqueous phases are extracted with 400 parts by volume of benzene. The combined benzene extracts are dried over anhydrous sodium sulfate, filtered and evaporated, to yield i3 157 parts of a thinly liquid diepoxide containing 6.5 epoxide equivalents per kg. (:88% of the theoretical).

The epoxide compound obtained by the procedure of this example has the formula EXAh/IPLE 12 99 parts of the dioxolane obtained from 1:2:4-butanetriol and M-tetrahydrobenzaldehyde are heated to about 45 C. and treated with 0.3 part by volume of boron trifluoride of about 48% strength in ether and dropwise with 46.3 parts of epichlorohydrin; the temperature is allowed to rise to 83 C. 15 minutes after completion of the addition of epichlorohydrin 2 parts of anhydrous sodium acetate are added, the whole is diluted with 250 parts of ethyl acetate and treated portionwise with 111 parts of peracetic acid. After the mixture has reacted for 6 hours at C. it is diluted with 200 parts by volume of ethylbenzene, washed twice with parts of water, treated with 750 parts by volume of ethylbenzene and evaporated in a 25 water-jet vacuum.

The resulting monoepoxide is dissolved in 250 parts by volume of benzene and 20 parts of finely powdered sodium hydroxide are added. The mixture is allowed to react for 2 hours at 2126 C. The sodium chloride formed is filtered off and the filtrate is washed with 50 parts by volume of a molar monosodium phosphate solution, dried over anhydrous sodium sulfate, filtered and evaporated, to yield a liquid diepoxide containing 5.86 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula o-crrn EXAMPLE 14 6 O 113 parts of the dioxolane obtained from 1:2:6-hexanetriol and A -tetrahydrobenzaldehyde are reacted in the presence of 0.3 part by volume of boron trifluoride of 48% strength in ether with 46.3 parts of epichlorohydrin at C.

After cooling, the product is treated with 2 parts of anhydrous sodium acetate and diluted with 300 parts of ethyl acetate. parts of peracetic acid are then added in portions and the mixture is allowed to react for 3 hours at 40 C., then diluted with 1000 parts by volume of ethylbenzene, washed twice with 150 parts of water, treated with another 500 parts by volume of ethylbenzene and evaporated in vacuo. The product is taken up in 500 parts by volume of benzene and dehydrohalogenated at 25 C. with 20 parts of finely powdered sodium hy- EXAMPLE 15 A mixture of 215 parts of distilled diglycerol, 300 parts of A -tetrahydrobenzaldehyde, 750 parts by volume of benzene, 3 parts of anhydrous zinc chloride and 3 parts by volume of phosphoric acid is boiled in a cyclic distillation apparatus while being stirred. After 4 hours 43 parts of water have separated. The mixture is filtered and evaporated, towards the end in a high vacuum at C., and there are obtained 430 parts of the bis-dioxolane.

A solution of the above dioxolane in 1500 parts by volume of benzene is treated with 20 parts of anhydrous sodium acetate. While stirring and cooling 550 parts of peracetic acid of 44.6% strength are added portionwise in the course of one hour at 30 C. The mixture is allowed to react for 2 hours at 30 C. and then cooled with ice. The solution of the epoxide is washed 3 times with 300 parts of water and twice with 300 parts by volume of 2 N-sodium carbon-ate solution until it is free from acid. The aqueous phases are extracted with 500 parts by volume of benzene. The benzene phases are combined, dried over anhydrous sodium sulfate and evaporated, to yield 399 parts of a thickly liquid diepoxide containing 4.55 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula OCH oH o CE /OH 0 o OCH CH 0 CH;;O 11,,

EXAMPLE 16 159 parts of crude diglycerol (obtained in known manner from glycerol and glycerolu-monochlorohydrin in the presence of sodium hydroxide solution) in 500 parts by volume of benzene are condensed with 220 parts of A -tetrahydrobenzaldehyde in the presence of 1 part of zinc chloride and 1 part by volume of concentrated phosphoric acid in a cyclic distillation apparatus, while 29 parts of Water separate.

The filtered solution of the bis-dioxolane is treated portionwise at about 30 C. in the course of /2 hour with 420 parts of peracetic acid. The mixture is allowed to react for 75 minutes at 30 C. and then washed with ice water and 2 N-sodium carbonate solution until it is free from :acid. The solution is dried over anhydrous sodium sulfate, filtered and evaporated. The residue is a highly viscous resin containing 4.62 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula on CH 0 0-011 CHO O CHz-O EXAMPLE 17 83 parts of distilled diglycerol are condensed in a cyclic distillation apparatus with parts of 6-methyl-A tetrahydrobenzaldehyde in the presence of 500 parts by volume of benzene, part of zinc chloride and 0.5 part by volume of concentrated phosphoric acid, during which parts of water separate. The solution is filtered and evaporated and the residue is distilled in a high vacuum, to yield 156 parts of bis-acetal boiling at 189- 199 C. under 0.2 mm. Hg pressure.

A solution of 141.5 parts of the bis-acetal in 500 parts of ethyl acetate is treated portionwise with 165 parts of peracetic acid. The temperature is maintained at 40 C., initially by cooling and then by supplying external heat. After 3 hours 97% of the theoretical amount of peracetic acid have been consumed. The mixture is cooled, diluted with 500 .parts by volume of ethylbenzene, washed twice with 150 parts of water, treated with 1000 parts by volume of ethylbenzene and evaporated under vacuum. The last remnants of the solvent are removed in a high vacuum at 120 C. Yield: 143 parts of an epoxy resin containing 3.75 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula /OCH (1112-0 a I O OCH o11o CH3 CH3- CH -OCH2 EXAMPLE 18 The bis-acetal obtained from 125 parts of 2:5-endomethylene-A -tetrahydrobenzaldehyde instead of from 6- methyl-M-tetrahydrobenzaldehyde by the method described in Example 17 boils at 202-204 C. under a pressure of 0.2 mm. Hg.

When the product is epoxidized for 3 hours, the theoretical amount of peracetic acid is consumed. The resulting diepoxide is an amorphous, brittle resin; its epoxide content cannot be determined by means of hydrogen bromide.

The epoxide compound obtained by the procedure of this example has the formula O-CH;

EXAMPLE 19 112 parts of glycerol-monotricyclodecenyl ether (adduct from dicyclopentadiene and glycerol) are condensed in a cyclic distillation apparatus in the presence of 0.3 part of zinc chloride, 03 part by volume of concentrated phosphoric acid and 500 parts by volume of benzene with 60 parts of A -tetrahydrobenzaldehyde. The solution of the acetal formed is filtered and evaporated and the residue is distilled, to yield 152 parts of a product boiling at 165172 C. under 0.02 mm. Hg pressure.

C H O calculated: C, 75.91%; H, 8.92%. Found: C, 75.80%; H, 8.88%.

A mixture of 111 parts of the above acetal and 300 parts of ethyl acetate is reacted for 5 hours at C. with 150 parts of peracetic acid, then cooled, diluted with 500 parts by volume of ethylbenzene and washed twice with 150 parts of Water. Another 500 parts by volume of ethylbenzene are added to the solution and the mixture is evaporated on a water bath in a water-jet vacuum, to yield a viscous diepoxide containing 5.22 epoxide equivalents per kg.

The epoxide compound obtained by the procedure of this example has the formula 16 EXAMPLE 20 A mixture of 180 parts of 3-vinyl-2:4-dioxospiro(5 :5 undecene-S (prepared by acetalizing A -cyclohexene- 1: l-dimethanol with acrolein) and 184 parts of A -tetrahydrobenz-al glycerol is heated to C., and 1 part of sulfuric acid is added, whereupon an evolution of heat is observed. The temperature is maintained for 2 /2 hours at C., first by cooling and then by heating. The acid is then neutralized with 1 part of anhydrous sodium carbonate. By heating the reaction product to 112 C. under 0.1 mm. Hg pressure only 6 parts of unreacted starting materials can be distilled off, that is to say that the additive combination proceeds substantially quantitatively. There are obtained 353 parts of the adduct in the form of a viscous, dark liquid.

A solution of 353 parts of the above adduct in 1050 parts of benzene is treated with 25 parts of anhydrous sodium acetate and heated to 35 C. In the course of 20 minutes 394 parts of peracetic acid of 41.2% strength are then added with vigorous stirring and the mixture is stirred for 2% hours at 35 C. and then cooled. The aqueous phase is separated, washed three times with 250 parts by volume of water, neutralized with 40 parts by volume of sodium hydroxide solution of 30% strength and finally washed twice with 150 parts by volume of Water. The benzene is distilled off and the product is freed from the last remnants of the solvent by being heated to C. under 0.1 mm. Hg pressure, to yield 320 parts of a viscous yellow liquid containing 4.75 epoxide equivalents per kg. (=94% of the theoretical) and consisting substantially of the diepoxide of the formula 65 parts of the epoxy resin prepared as described in Example 3 are melted at C. with 28.9 parts of phthalic anhydride and poured into an aluminum mould (40 x 10 x 140 mm.).

The mixture is cured for 3 hours at 120 C., then for 3 hours at 160 C. and finally for 24 hours at 200 C. The resulting moulding has the following properties:

Bending strength 11.6 kg./sq. mm. Impact bending strength 13.5 cm. kg./sq. cm. Thermal stability according to Martens C.

EXAMPLE 22 75 parts of the diepoxide prepared as described in Example 7 and 18.8 parts of succinic anhydride are melted at 120 C. and poured into an aluminum mould (40 X 10 X mm.).

The mixture is cured {or 16 hours at 120 C., then for 6 hours at C. and finally for 12 hours at 200 C. The resulting moulding has the following properties:

Bending strength 9.0 kg./sq. mm. Impact bending strength 6.8 cm. kg./sq. cm. Thermal stability according to Martens C.

EXAMPLE 23 65 parts of the diepoxide prepared as described in Example 15 are melted with 28.4 parts of phthalic anhydride at 120130 C. and poured into an aluminum mould (40 x 10 x 140 mm.).

The mixture is cured for 24 hours at 140 C. and then for 24 hours at 200 C. The resulting moulding has the following properties:

Bending strength 10.1 kg./Sq. mm.

1 7 Impact bending strength 7.9 cm. k-g./sq. cm. Thermal stability according to Martens 187 C.

EXAMPLE 24 70 parts of the diepoxide prepared as described in Example 15 are melted with 21.2 parts of phthalic anhydride at 120 C. The resulting mixture has at 120 C. a viscosity below 20 centipoises and after 65 minutes of 1500 centipoises. The melt is poured over plates of glass to form layers 0. 1 mm. and 1 mm. thick respectively and then hardened for 24 hours at 140 C. and subsequently for 2-4 hours at 200 C. The cured films are clear, substantially colorless, elastic and adhere very firmly to the support. They remain intact after having been immersed for one hour at room temperature in 5 N-sulfuric acid, 5 N-sodium hydroxide solution, water, acetone and chloro'benzene.

EXAMPLE 25 74 parts of the epoxy resin prepared as described in Example 16 and 32.8 parts of phthalic anhydride are melted at 120 C. and poured into an aluminum mould (40 x 10 x 140 mm).

The mixture is cured for 24 hours at 140 C. The resulting moulding has the following properties:

Bending strength 8.1 kg./sq. mm. Impact bending strength 3.8 cm. kg./sq. cm. Thermal stability according to Martens 173 C.

EXAMPLE 26 68.5 parts of the epoxy resin prepared as described in Example 10 are melted at 120 C. with 36.5 parts of phthalic anhydride and poured into an aluminum mould (40 x 10 x 140 mm.). The mixture is cured for 4 hours at 80 C. and then for 24 hours at 140 C. The resulting moulding has the following properties:

Bending strength 10.9 kg./sq. mm. Impact bending strength 12.1 cm. kg./sq. cm. Thermal stability according to Martens 147 C.

What is claimed is: 1. A diepoxide of the formula in which R to R and R are hydrogen and together R and R form the methylene group, R is a member selected from the group consisting of hydrogen and methyl, Z represents the hydrocarbon radical obtained by removing the hydroxyl groups from a saturated aliphatic trihydric alcohol with 3 to 6 carbon atoms and A is a member selected from the group consisting of the glycidyl group, the group of the formula and the group of the formula R-CH wherein R is a member selected from the group consisting of hydrogen and methyl, and wherein the cyclic acetal moiety his 2- consists of at least five and at most six ring members.

2. The compound of the formula 3. The compound of the formula 4. The compound of the formula O-CH 0% l O 0-H 7. The compound of the formula The compound of the formula \OOH (JEy-O-OH CHr-C No references cited.

WALTER A. MODANCE, Primary Examiner. 

1. A DIEPOXIDE OF THE FORMULA 